| Specification |
H17A |
H17D |
H17O |
H17M |
| Weight (kg) |
7,5 |
13,5 |
7,5 |
7,0 |
Dimension
(WxDxH) (mm) |
214x255x300 |
214x255x350 |
214x255x300 |
214x255x300 |
| Resolution |
0.1 units |
| Indenter shape |
35° Cone (Frustum) |
30° Cone |
1/2 Spherical |
30° Cone |
| Indenter radius |
Flat |
0.1 mm |
1.19mm |
0.79mm |
| Full scale |
2.5 mm |
2.5 mm |
2.5 mm |
1.25 mm |
| Force method |
Spring |
Max. İndentor
force |
8.05 N |
44.45 N |
8.05 N |
0.765 N |
| Force duration |
1 or 3 seconds |
Minimum sample
thickness |
6 mm |
6 mm |
6 mm |
1.25 mm |
| Standards |
Shore A Scale: BS ISO 7619, DIN 53505, ISO 7619, ASTM D2240, JIS 6301,
Shore O Scale: ASTM D2240, Shore D Scale: ASTM S2240, Shore M Scale: ASTM D2240 |
| Shore Type |
Force |
Standard |
Contact
Force |
Indentor Shape |
Measurement
Height |
Material
Thickness |
Measurement
Range |
Application Material |
| WA17A (*) |
8.05 N |
ASTM D 2240
ISO 7619-1 |
1000 g |
35° Cone (Frustum) |
2.50 mm |
8 - 10 mm |
20 - 90 A |
Soft, vulcanized rubber, natural rubber,nitriles,
thermoplastic elastomers, flexible polyacrylics and thermosets, wax, felt and leathers. |
| WA17B (*) |
8.05 N |
ASTM D 2240
ISO 7619-1 |
1000 g |
30° Cone |
2.50 mm |
8 - 10 mm |
Above 90 A
Below 20 D |
Moderately hard rubber, thermoplastic elastomers, paper products and fibrous materials. |
| WA17C (*) |
44.5 N |
ASTM D 2240
ISO 7619-1 |
5000 g |
35° Truncated Cone
(Frustum) |
2.50 mm |
8 - 10 mm |
Above 90 A
Below 20 D |
Medium hard rubber, thermoplastic elastomers, medium hard plastics and thermoplastics. |
| WA17D (*) |
44.5 N |
ASTM D 2240
ISO 7619-1 |
5000 g |
30° Cone |
2.50 mm |
8 - 10 mm |
Above 90 A |
Hard rubber, thermoplastic elastomers, harder plastics and ridgid thermoplastics. |
| WA17DO (**) |
44.5 N |
ASTM D 2240
ISO 7619-1 |
5000 g |
2.38 mm 1/2 Sphere |
2.50 mm |
8 - 10 mm |
Above 90 A
Below 20 D |
Moderatly hard rubber, thermoplastic elastomers, and very dense windings. |
| WA17M (*) |
0.764 N |
ASTM D 2240
ISO 7619-1 |
250 g |
30° Cone |
1.25 mm |
2.0±0.5 mm |
20 - 85 A |
Thin, irregularly shaped rubber, "O" rings,thermoplastic elastomers and plastic specimens. |
Current Standard Instrument (*)
Standard Instrument would only require a different indentor (**)
This instrument would requie a different spring compression and weight (***)